An iron specimen is plastically deformed in shear by 1%, and it has u dislocation density of
- Calculate the magnitude of the Burger's vector for these dislocations in iron.
- Calculate the average distance moved by the mobile dislocations as a result of the 1% shear strain.
Want to see the full answer?
Check out a sample textbook solutionChapter 6 Solutions
Materials Science And Engineering Properties
- FCC single crystal is alligned such that [001] is parallel to the stress axis, σ=100MPa.arrow_forwardIn a brittle material, the ultimate stress is equal to the breaking stress. A True B Falsearrow_forwardNarrow bars of aluminum are bonded to the two sides of a thick steel plate as shown. Initially, at T₁ = 70°F, all stresses are zero. Knowing that the temperature will be slowly raised to T₂ and then reduced to T₁, determine (a) the highest temperature T₂ that does not result in residual stresses, (b) the temperature T₂ that will result in a residual stress in the aluminum equal to 58 ksi. Assume aa = 12.8 x 10-6/°F for the aluminum and a = 6.5 × 10-6/°F for the steel. Further assume that the aluminum is elastoplastic with E = 10.9 × 106 psi and ay = 58 ksi. (Hint: Neglect the small stresses in the plate.) Fig. P2.121arrow_forward
- At an axial load of 22 kN, a 15-mm-thick × 50-mm-wide polyimide polymer bar elongates 5.7 mm while the bar width contracts 0.15 mm. The bar is 245-mm long. At the 22-kN load, the stress in the polymer bar is less than its proportional limit. Determine Poisson’s ratio.arrow_forwardAn aluminium specimen with an initial gauge diameter d, = 10 mm and gauge length, 1, = 100 mm is %3D subjected to tension test. A tensile force P= 50 kN is applied at the ends of the specimen as shown, resulting in an elongation of 1 mm in gauge length. The Poisson's ratio (µ) of the specimen is Take shear modulus of material, G = 25 GPa. Consider engineering stress-strain conditions. Parrow_forward1) Please indicate in the stress-strain diagram given below the stress levels that can cause creep. 2) The effect of an increase in service temperature or applied stress is to shift the 3) Dislocation density . In Region number (...) while creep deformation is increasing at an increasing rate. 4) Dislocation density is remains constant in Region number (.) while the creep rate is increasing. 5) For some applications the amount of creep in Region number (.) is taken as the design criteria.arrow_forward
- Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning