Question
Chapter 38, Problem 3P
(a)
To determine
The importance of the deposited metal to match with the material being repaired.
(b)
To determine
The differ properties of the deposited material from those of the material being repaired.
(c)
To determine
The concerns one may have relating to heat affected zone or residual stresses.
(d)
To determine
The requirement of the post-repair processing technique.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
Identify the mold die material in order to produce the low melting casting product like
aluminium, copper and silver.
Plastics
Graphite
Wood
Cast iron
State the steps that must be taken to correct the following casting defects:
1. Formation of discontinuity in the casting.-
2. Cast surface consisting of a mixture of sand and metal.
3. Casting with balloon-shaped gas cavity near the surface.
4. Formation of hot tearing in expandable and permanent mold casungs.
5. Metal splatters during pouring and solid globules form and become entrapped in
casting.
What is the typical industrial reduction ratio for an ingot while being processed into a forging?
Group of answer choices
7:2
3:1
2:1
10:1
How are oxides removed from the melt pool during a casting process?
Group of answer choices
Machined after solidification
Collected in slag
Allowed to diffuse out into the air
Vacuum degassing
Chapter 38 Solutions
Degarmo's Materials And Processes In Manufacturing
Ch. 38 - What are some joining conditions where welding...Ch. 38 - What are some of the lower-temperature methods of...Ch. 38 - In what ways is a thermit weld similar to the...Ch. 38 - What is the source of the welding heat in thermit...Ch. 38 - For what types of applications might thermit...Ch. 38 - What is the source of the welding heat in...Ch. 38 - What are some of the various functions of the slag...Ch. 38 - Electroslag welding would be most attractive for...Ch. 38 - What is the source of heat in electron-beam...Ch. 38 - Why is a high vacuum required in the electron-beam...
Ch. 38 - What types of production limitations are imposed...Ch. 38 - What are the major assets and negative features of...Ch. 38 - What are some of the attractive features of...Ch. 38 - What is unique about the fusion zone geometry of...Ch. 38 - Describe the weld pool geometry and size of the...Ch. 38 - What is an autogenous weld?Ch. 38 - What might be necessary to permit the laser...Ch. 38 - What are some of the Ways in which laser-beam...Ch. 38 - What are the three common types of industrial...Ch. 38 - Which type of laser light can be transmitted...Ch. 38 - What are some of the attractive features of a...Ch. 38 - Why is laser-beam welding an attractive process...Ch. 38 - What are the attractive properties of hybrid...Ch. 38 - Prob. 24RQCh. 38 - What is the function of the assist gas in...Ch. 38 - What is the difference between exothermic cutting...Ch. 38 - Which type of laser is preferred for cutting...Ch. 38 - Prob. 28RQCh. 38 - Prob. 29RQCh. 38 - What features have made lasers a common means of...Ch. 38 - What are some of the attractive features of laser...Ch. 38 - What are some common objectives of surfacing...Ch. 38 - What types of materials are applied by surfacing...Ch. 38 - Prob. 34RQCh. 38 - What is the benefit of high-velocity oxyfuel...Ch. 38 - What are some of the arc or plasma techniques that...Ch. 38 - How is thermal spraying similar to surfacing? How...Ch. 38 - Prob. 38RQCh. 38 - Prob. 39RQCh. 38 - Provide a reasonable definition of brazing?Ch. 38 - What are some key differences between brazing and...Ch. 38 - What kinds of materials or combinations can be...Ch. 38 - What advantages can be gained by the lower...Ch. 38 - Why do brazed joints have an enhanced...Ch. 38 - What is the most important factor influencing the...Ch. 38 - How does capillary action relate to joint...Ch. 38 - Why is it necessary to adjust the initial...Ch. 38 - What is wettability? Fluidity? How do each relate...Ch. 38 - What are the two most common types of brazed...Ch. 38 - How do the butt-lap and scarf joint configurations...Ch. 38 - What are some important considerations when...Ch. 38 - What are some of the most commonly used brazing...Ch. 38 - Why are eutectic alloys attractive as brazing...Ch. 38 - What special measures should be taken when brazing...Ch. 38 - What are the three primary functions of a brazing...Ch. 38 - Why is it important to preclean brazing surfaces...Ch. 38 - How might braze metal be preloaded into joints?Ch. 38 - What is the purpose of brazing jigs and fixtures?Ch. 38 - 59- What are some factors to consider when...Ch. 38 - What are the advantages and disadvantages of torch...Ch. 38 - What is the primary attraction of furnace-brazing...Ch. 38 - Why might reducing atmospheres or a vacuum be...Ch. 38 - What are some of the attractive features of...Ch. 38 - Why is dip brazing usually restricted to use with...Ch. 38 - What are some of the attractive features of...Ch. 38 - Why is flux removal a necessary part of many...Ch. 38 - What benefits can be achieved through fluxless...Ch. 38 - How does braze welding differ from traditional...Ch. 38 - What is the primary difference between brazing and...Ch. 38 - What are the six steps of a soldering operation?Ch. 38 - Why is soldering unattractive if a high-strength...Ch. 38 - For many years, the most common solders have been...Ch. 38 - What is driving the conversion to lead-free...Ch. 38 - What are some of the difficulties encountered when...Ch. 38 - What are the two basic families of soldering flux?Ch. 38 - What are some of the more common heat sources for...Ch. 38 - Why is wave soldering attractive for making the...Ch. 38 - Describe the vapor-phase soldering process.Ch. 38 - A common problem with brazed or soldered joints is...Ch. 38 - When molten metal deposition is applied to a...Ch. 38 - Prob. 3P
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- With free body diagram please. Also, no explanation, direct clean solution please thankyouarrow_forwardنقطة واحدة The third sequence in the Injection machine of polymers, a shot of melt, which has been brought to the right temperature and viscosity by heating and the mechanical working of the screw, is injected under high pressure into the mold .cavity TO FO * Coppola is used to convert pig iron to gray .cast iron TO F LLarrow_forwardWhich among the following design considerations for casting to be followed to reduce stress concentration in parts? O a. Shape the casting for orderly solidification O b. Avoid abrupt changes in cross section Oc Avoid thin sections O d. Make provision for easy removal of pattern from the mouldarrow_forward
- لانقطة واحدة of Warm working The advantages over cold working are: 1) forces and power are higher,2) more intricate work geometries possible, and 3) need for annealing may be reduced .or eliminated T F Blow molding is an important industrial process for making one- piece hollow plastic parts with thick .walls T Sly The sequence of the Blow Molding is automated and often integrated with downstream operations such .as bottle filling and labeling T لنقطة واحدةarrow_forwardFor casting processes in metals, which of the following are true? (This question has more than one correct answer) a. May involve a multi-step casting process with an initial prototype used to shape the mould b. Can lead to internal defects in the metal c. Leads to formation of a solid part consisting of fused precursor particles d. Requires materials with high toughness to resist deformation e. Can only be used to form simple shapesarrow_forwardManufacturing Processes How to perform the sand casting of hollow piece and how to verify the calculated solidification time?arrow_forward
- Converging passage is used for feeding the liquid molten metal into the mould to (a) increase the rate of feeding (b) quickly break off the protruding portion of the casting (c) decrease wastage of cast metal (d) avoid aspiration of airarrow_forward(LDM) B-Write (True) or (False) for the following sentences: 1. Cast-cobalt Alloys tool are produced by powder me X کت تي سبون لولاعة metallurgy. tool at tool from rubbing the work positive rake angles on tools are provided. X 2. In order to prevent 3. A fine grained grinding wheel is used to grind hard materials. X 4. when the proportion of pores is re volume, the structure is dense. 5. Chills are used to increase the heating rate of metal. يم التقدم على امن وامي is relatively larger than proportion of abrasive grains in the wheelarrow_forward2) With neat sketch explain the working of Hot chamber die castingarrow_forward
- Please give a detailed solution and each step cleanly Thank youarrow_forwardThe primary function of a riser is to (a) feed molten metal to casting as it solidifies (b) prevent atmospheric air from contaminating the metal in the mould (c) allow gases to easily escape from mould cavity D)allow molten metal to rise above the mould cavityarrow_forward2.1 What is the benefit of using investment casting for the production of a turbine rotorcompared to other casting processes?2.2 Which AM materials and processes (according to the ISO/ASTM 52900 standard) ismostly used during the manufacturing of patterns for the investment casting process?List the advantages and disadvantages of each of the AM processes.2.3 What are the advantages and disadvantages of using AM techniques to producepatterns for the investment casting process, compared to conventional methods?2.4 Show with a sketch, how the build orientation of the processes listed in Question 2.2can have an influence on the accuracy and surface quality of a pattern.2.5 Which manufacturing process (listed in Question 2.2) will be most suitable to producea pattern for the turbine rotor? Provide reasons for your selection.2.6 The use of additive manufactured patterns for the investment casting process arebeing used more frequently in industry. Using this technology, comment onproduction…arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Force | Free Body Diagrams | Physics | Don't Memorise; Author: Don't Memorise;https://www.youtube.com/watch?v=4Bwwq1munB0;License: Standard YouTube License, CC-BY