Turbine blade is made from aluminum alloy A356. The blade showed 35MPam of fracture toughness and 250 MPa of stress resulted at maximum internal crack 1 ength 2.0 mm. For this same component and alloy compute the fracture toughness if the stress level reach to (your student IDX 10) MPa when the maximum intemal crack length became 1.0 mm.

Turbine blade is made from aluminum alloy A356. The blade showed 35MPam of fracture toughness and 250 MPa of stress resulted at maximum internal crack 1 ength 2.0 mm. For this same component and alloy compute the fracture toughness if the stress level reach to (your student IDX 10) MPa when the maximum intemal crack length became 1.0 mm.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A Plexiglas model of a gear has a 1 mm crack formed in its fillet curve (where the tensile stress is maximum). The model is loaded until the crack starts to propagate. Y=1.5. How much higher a lod can a gear (made of AISI 4340 steel tempered to 425°C) carray with the same crack and the same geometry?
ASAP
Compute the minimum critical surface crack (edge crack) length if the fatigue life must be a minimum of 5.0 x 106 cycles. Assume the initial maximum edge surface crack length of 1.80 mm and a maximum tensile stress of 160 MPa and minimum stress of 0 MPa. Assume m = 1.8 and A= 7.5 x 1013 in MPa and meter units, Assume Y= 1.25. O a. 4.26 mm O b. 5.38 mm OC. 2.36 mm O d.0.125 m
Q2:- The part of the vehicle is production from an magnesium alloy .if KIC 40 MPavm. The fracture occurred at a pressure of 195 MPa when the maximum edge crack length was 3.0 mm. Calculate the value Y. If a stress levelis increased to 275 MPa and the maximum edge crack length is reduced to 2.3 mm, predict whether any fracture will occur. Compare your answer with existing data. Justify your answer.
The flexural (or fracture) strength of brittle materials may be determined using a variation ofEquation 8.1. Compute the critical crack tip radius (row sub t in nm) for an Al2O3 specimen thatexperiences tensile fracture at an applied stress (sigma initial) of 275 MPa. Assume a critical surfacecrack length (a) of 2 * 10^-3 mm and a theoretical fracture strength of E/10, where E is themodulus of elasticity (393 GPa). Note, fracture will occur when sigma sub m reaches the theoreticalfracture strength of the material.given equation: sigma sub n = 2*sigma initial*sqrt(a/row sub t)
urrent Attempt in Progress 1 X Incorrect. Calculate the maximum internal crack length allowable for a Ti-6Al-4V titanium alloy component that is loaded to a stress one-half of its yield strength. Assume a yield strength 910 MPa, a plane strain fracture toughness of 55 MPam and that Y = 1.47. 2 2.96 eTextbook and Media Hint Save for Later W S ** F2 X #3 I E D 20 F3 $ 4 C mm R F olo Lo % 5 V T G
The part of the vehicle is production from an magnesium alloy ,if KIC 40 MPa√m. The fracture occurred at a pressure of 195 MPa when the maximum edge crack length was 3.0 mm. Calculate the value Y. If a stress level is increased to 275 MPa and the maximum edge crack length is reduced to 2.3 mm, predict whether any fracture will occur. Compare your answer with existing data. Justify your answer
la. In the design of a pressure vessel, the leak-before-break criterion is used considering the circumferential wall thickness and the plain strain fracture toughness. The design is limited by the yield strength gs and the factor of safety (SF). Derive expressions for the critical crack size. 1b. Calculate the design stress and stress intensity factor if the safety factor is 1.5. Data: gxS = 586 MPa and KIC = 33 MPa m1/2.
Question 2 A machine component is made of Aluminium alloy having an ultimate tensile stress Ou = 350MPa, a fracture toughness Kic= 40 MPa√m and a geometry factor Y=1.12. The component is subject to cyclic tensile stress of 200 MPa and cyclic compressive stress of 70 MPa. Before the operation, using an ultrasonic non-destructive testing technique, it was found that there is an edge crack of length 2mm. The crack growth C(AK)m, where is in m/cycle, AK ΔσΥ νπα , C ~ 2.2×10-12 da rate is given by da dN dN and m=3.2. Find the critical crack length. = =
Using the tensile test simulation tool, a. generate the stress-strain curve for aluminum b. Indicate the following points in the stress-strain curve for aluminum and give the corresponding values: limit of proportionality elastic limit 0.2% offset yield stress (include the graph illustrating how this was determined) ultimate stress fracture stress c. Calculate modulus of elasticity. d. compare aluminum with nylon (include the related graph) and answer the following: Which has higher tensile strength? Provide the necessary values to support the answer. Which is stiffer? Support your answer with calculations.
The engineering stress-engineering strain tensile curve for a stainless steel type 304 alloy is shown. Calculate the constants K and n for the true stress and true strain curve before necking (or = K (&)"). Engineering Stress (MPa) 1000 900- 800- 700- 600- 500- 400- 300- 200- 100- of 0.0 02 0.4 Enginering Strain (mm/mm) 0.6 0.8 1.0
Q5/ The Stress-strain diagram of any ductile metal or alloys reveals several critical points. Based on your understanding of this diagram, plot it schematically (without scale) and specify the following points: 1. Tensile streng th 2. Yield strength 3. At what stage the necking occurs 4. The fracture strength 5. The elastic zone 6. The Plastic zone 7. Young modulus of elasticity