A metal alloy cylindrical specimen was tested in a lab and its o-e plot is shown below. The diameter and length of the specimen were 6 mm and 90 mm respectively and Poison ratio of the alloy is 0.28. Calculate ductility in terms of %AR and %EL when the alloy was loaded upto Elastic Point corresponding to stress of 180 MPa.

A metal alloy cylindrical specimen was tested in a lab and its o-e plot is shown below. The diameter and length of the specimen were 6 mm and 90 mm respectively and Poison ratio of the alloy is 0.28. Calculate ductility in terms of %AR and %EL when the alloy was loaded upto Elastic Point corresponding to stress of 180 MPa.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

O The following engineering stress-strain data were obtained for a 0.2% C plain-carbon steel. (i) Plot the engineering stress-strain curve. (ii) Determine the ultimate tensile strength of the alloy. (iii) Determine the percent elongation at fracture. Engineering Engineering Engineering Engineering Stress Strain Stress Strain (ksi) (in./in.) (ksi) (in./in.) 76 0.08 30 0.001 75 0.10 55 0.002 73 0.12 60 0.005 69 0.14 68 0.010 65 0.16 72 0.020 56 0.18 74 0.040 51 0.19 75 0.060 (Fracture)
al 72% Í 22:39 365 3bed sleimen 10 minutes ago Question 1 Determine the percentage of ductility of a metal alloy having the following tensile stress-strain diagram. Not yer answered Stress-Strain Diagram Marked out of 15.00 P lag question 025 Strain jem/em Select one: O 25% O 0.26
The engineering stress-strain curve below was obtained for a precipitation hardened Aluminum alloy. What is the approximate Yield Strength for this alloy in psi? Engineering Stress Based on Original Area (psi) 50,000 45,000 40,000 35,000 30,000 25,000 20,000 15,000 10,000 5,000 0 O 0.02 0.04 0.06 Aluminum 6061-T6 0.08 0.1 0.12 Engineering Strain (in/in) 0.14 X 0.16 0.18
A steel ruler of 40 cm, calibrated at 27°C, was used to measure a component in a relatively hot environment of 65°C. What would be the error % in the measurements if a .steel=17.7x10-6 °C^-1
In tensile test a plain carbon steel specimen has a (40mm) gauge length and the Final area (A final) of specimen after tensile test was 264.327. The load which caused fracture was (122.5 KN). After fracture, the final length was 47.516mm True stress at fracture is. * O 463.441 N/mm2, O 525.441 N/mm2, O 254.441 N/mm2, 498.441 N/mm2,
6. The following engineering stress-strain data were obtained for 0.2% C plain carbon steel. (a) Plot the engineering stress-strain curve (b) Determine the ultimate tensile strength for the alloy (c) Determine the percent elongation at fracture (d) Plot the true stress-strain curve Engineering strain, in./in. Engineering stress, ksi 30 0.001 55 0.002 60 0.005 68 0.01 72 0.02 74 0.04 75 0.06 76 0.08 75 0.1 73 0.12 69 0.14 65 0.16 56 0.18 51 0.19(fracture)
Determine the percentage of ductility of a metal alloy having the following tensile stress-strain diagram. 600 500E 400 500 300 400E 300 200 200 100 100 0.000 0.002 0.004 0.006 Strain 0.00 0.04 0.08 0.12 0.16 0.20 Strain EN Stress (MPa) Stress (MPa)
Using the tensile test simulation tool, a. generate the stress-strain curve for aluminum b. Indicate the following points in the stress-strain curve for aluminum and give the corresponding values: limit of proportionality elastic limit 0.2% offset yield stress (include the graph illustrating how this was determined) ultimate stress fracture stress c. Calculate modulus of elasticity. d. compare aluminum with nylon (include the related graph) and answer the following: Which has higher tensile strength? Provide the necessary values to support the answer. Which is stiffer? Support your answer with calculations.
A tensile test specimen of stainless steel alloy having a diameter of 0.495 in. and a gage length of 2.00 in. was tested to fracture. Stress and strain data obtained during the test are shown. Determine the proportional limit. Stress (ksi) 40 30- 20 10- 0- 0.0 0.0 Upper scale 0.020 0.002 22 ksi O 15 ksi E 19 ksi O 10 ksi 13 ksi Lower scale- 0.040 0.060 0.080 0.100 0.004 0.006 0.008 0.010 Strain (in./in.) 0.120 0.012
Question-7. Steady-state creep data taken for an alloy at a stress level of 160 MPa are given below. The stress exponent n for the alloy is 6.8. R is 8.3145 J/mol-K. Compute the steady-state creep rate at 1000 °C and a stress level of 68 MPa. Es (h-1) 6.8 × 10-5 T (°C) 800 8.6 x 10-3 900
ASAP
Consider a cylindrical specimen of a steel alloy with 8.5 mm diameter and 80 mm long that is pulled in tension. Estimate the following mechanical properties using Fig. 1: a. Modulus of Elasticity and Resilience in MPa and psi b. Ultimate Tensile Strength in MPa and psi c. Fracture Strength in MPa and psi d. Ductility or % elongation at fracture in MPa and psi 2000 10³ psi MPa 300 2000 200 1000 100 0 0.000 0.005 0.010 0.015 Strain 0.020 0.040 0.060 Strain Fig. 1 Engineering Stress-Strain Curve Stress (MPa) 1000 0 0.000 Stress 0.080 300 200 100 0 Stress (10³ psi)