Forging: A cylindrical specimen made of annealed 4135 steel (K = 1015 MPa, n = 0.17) has a diameter of 150 mm, and is 100 mm high. It is upset between dies to a height of 50 mm at room temperature. Calculate the work done for 2 cases: a) Ideal (frictionless) b) Friction, where the coefficient of friction is 0.2. Set up on paper and solve using software. Be careful with units.

Forging: A cylindrical specimen made of annealed 4135 steel (K = 1015 MPa, n = 0.17) has a diameter of 150 mm, and is 100 mm high. It is upset between dies to a height of 50 mm at room temperature. Calculate the work done for 2 cases: a) Ideal (frictionless) b) Friction, where the coefficient of friction is 0.2. Set up on paper and solve using software. Be careful with units.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A compression test is performed on a 2” diameter by 5” long bar of an unknown metal. At the end of the compression test, the bar has a height of 3.5 inches. The strength coefficient (K) and the work hardening coefficient (n ) are 250 MPa and 0.4, respectively. State all assumptions needed to work the problem. a) Calculate the final diameter of the bar in inches. b) Calculate the flow stress in MPa when the length of the bar is 4”.
7. A strip of annealed low-carbon steel (K = 528 MPa, n = 0.25) is rolled from its initial dimensions (210 mm wide and 13 mm thick) to a thickness of 7 mm. The rollers have a radius of 250 mm, the roller rotates at 200 rpm, and u = 0.1. Compare this high frictional force and power with the low frictional (u = 0) forces and power. a. Estimate the roll force and power required for this process.
In a stamping operation, a 2 mm thick stainless steel sheet with an ultimate tensile strenght of 900 MPa is used. For a given blank size of 200 mm x 200 mm, calculate the punching force required to make a sheet metal part with 20 circle holes, each 4 mm and 10 square holes each with an edge of 5 mm. (1)
In a single pass rolling bearing process using 510mm diameter steel rollers a strip of width 110mm and thickness 6mm undergoes 20%reduction of thickness. Find the angle of bite
A solid piece of steel 60 mm in diameter and 80 mm height is reduced in height by 50 percent with the help of open die forging. The work material characteristics are represented by k = 350MPA and n = 0.16. If coefficient of friction is 0.1, find the maximum forging force.
A compound die will be used to blank and punch a large rectangle (90x150mm blank dimensions) out of 6061ST aluminum alloy sheet stock 3.5 mm thick. The diameter of inside hole is 25 mm. The aluminum sheet metal has a tensile strength 310 MPa. Determine the minimum tonnage press (force) to perform the blanking and punching operation (1) assume that blanking and punching occur simultaneously and (2) assume that punching occurs first, then blanking, Take: Ac-0.06
A mechanical press is powered by a 23-kW motor and operates at 40 strokes per minute. It uses a flywheel, so that the crankshaft speed does not vary appreciably during the stroke. If the stroke is 150 mm, what is the maxumum const.ant force rhat can be exerted over the entire stroke length?
An aluminium strip with a cross section of 200 mm × 8 mm is being rolled with 25% reduction of area, using 400 mm diameter steel rolls. The tensile yield stress of aluminium is 0.28 kN/mm2. Calculate i) The angle subtended by the deformation zone at the roll center. ii) The minimum coefficient of friction between the workpiece and the rolls for an unaided bite to be possible.
Question 1 solid cylindrical work piece is reduced in height by an open die forging process using flat dies on a mechanical press, powered by a 20 kW motor which operates at 35 strokes per minute with a stroke length of 160 mm. The work piece is 60 mm high and 100 mm in diameter and is to be reduced in height by 15%. The coefficient of friction during the operation is 0,18. Calculate the flow stress of work piece material if the press is set to operate at 90% of its maximum capacity.
A 42mm thick low carbon steel plate is reduced to 34mm in one rolling pass. At the same time that the thickness is reduced, the plate is widened by 4%. The elastic limit of the steel plate is 174MPa and its resistance is 290MPa. The input speed of the plate is 15m/min. The radius of the cylinder is 52.8mm and the rotation speed is 49 revolutions per minute. Determine: a) The minimum coefficient of friction that will make this rolling operation possible. b) The output speed of the plate c) Slide forward
9. A rectangular hole of size 100 mm x 50 mm is to be made on a 5 mm thick sheet of steel having ultimate tensile strength and shear strength of 500 MPa and 300 MPa, respectively. The hole is made by punching process. Neglecting the effect of clearance, the punching force (in kN) is
Find the rolling resistance (in N) when: the rolling coef. is 0.020, the effective mass is 156 kg.