A NIO-20 mol % Mgo ceramic is allowed to solidify. (See the figure below.)Temperature (°C)280026002400-22002000L(Ni, Mg)040 60 80 MgOMole percent MgONIO 20(a) Determine the composition (in mol% MgO) of the first solid to form.80x(b) Determine the composition (in mol% MgO) of the last liquid to solidify under equilibrium conditions.35X%

(a) Determine the composition (in mos MD) of the first sold to form (b) Determine the composition…

A NIO-20 mot% Mgo ceramic is allowed to solidify. (See the figure below.) Temperature (°C) 2800 2600 2400- 2200 2000 L (Ni, Mg)0 NIO 20 40 60 80 MgO Mole percent MgO (a) Determine the composition (in mol% MgO) of the first solid to form. 80 x (b) Determine the composition (in mol% MgO) of the last liquid to solidify under equilibrium conditions. 35 X%

A NIO-20 mot% Mgo ceramic is allowed to solidify. (See the figure below.) Temperature (°C) 2800 2600 2400- 2200 2000 L (Ni, Mg)0 NIO 20 40 60 80 MgO Mole percent MgO (a) Determine the composition (in mol% MgO) of the first solid to form. 80 x (b) Determine the composition (in mol% MgO) of the last liquid to solidify under equilibrium conditions. 35 X%

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

2. a) How many kilograms of nickel must be added to 1.75 kg of copper to yield a liquidus temperature of 1300 °C? b) How many kilograms of nickel must be added to 5.43 kg of copper to yield a solidus temperature of 1200 °C? c) The solidus and liquidus temperatures for the copper-gold system are given here. Construct the phase diagram for this system and label each region. Composition (wt.% Au) Solidus Temperature (C) Liquidus Temperature (C) 1085 1085 1019 972 20 1042 996 946 40 60 934 80 911 911 90 928 942 95 974 984 100 1064 1064
Temperature ("C) Temperature ($1 Consider 1 kg of Copper - Silver alloy (Cu - Ag) containing 75 wt% Ag. The phase diagram of the alloy is shown in the figure below. The alloy is cooled to 778 °C (just below the eutectic temperature). Calculate the mass in kg of the eutectic phase B (phase B that appears during the eutectic reaction) that forms? Composition (at% Ag 20 40 60 100 2200 80 1200 2000 Liquidus 1000 LIquid 1800 Solidus 1600 800 779°C (T 80 91.2 1400 IC. 1200 600 Solvus T000 400 800 200 20 40 80 100 (Cu) Composioon wt A
At what temperature does the first liquid phase form at 90% Ni? T(°C) 1600 1500 1400 1300 1200 1100 1000, L (liquid) L+α solidus liquidus 80 100 20 40 60 80 wt% Ni
A 50 wt% Pb-50 wt% Mg alloy is slowly cooled from 700 °C (1290 °F) to 400 °C (750 °F). (a) At what temperature does the first solid phase form? (b) What is the composition of this solid phase? (c) At what temperature does the liquid solidify? (d) What is the composition of this last remaining liquid phase? Temperature (°C) 700 600 500 400 300 200 100 2 0 0 (Mg) 560°C First solid (21 wt% Pb) α 20 465°C 5 a + L Composition (at% Pb) 40 10 L a + Mg₂Pb 20 60 Composition (wt% Pb) Last liquid (67 wt% Pb) 30 Mg₂Pb 40 T T L + Mg₂Pb M 18 80 L + Mg₂Pb 70 100 B B+ Mg₂Pb T B + L D T 1200 1000 800 600 400 200 100 (Pb) Temperature (°F)
Decarburization of a steel occurs when carbon diffuses from the steel to the surface and enters the atmosphere. How long will it take for a 0.6 % C steel surface to decarburize below 0.1 % C for a depth of 2 mm if the FCC steel is held at 1250 °C in an atmosphere containing zero carbon? I need this question's answer. It's important for me.
A copper-nickel alloy contains 38% by weight of Cu and 62% by weight of Ni and is at 1330 ° C. Using the figure, answer the following questions:a) What is the percentage by weight of copper in the solid and liquid phases at this temperature?b) What percentage by weight of the alloy is liquid and what percentage is solid?
In an Al casting ingot containing 2wt.% Cu, the content of Cu at grain boundaries has reached 12wt.%. How long this ingot should be held at 530 K to attain a difference of 10% in Cu concentration between center and boundary of the grains. The mean distance from the center of grains to the boundary is 100μm. Du= 3.9x10⁹ cm²/sec
Using the following table, draw a melting point diagram and estimate the eutectic temperature and composition: Percent composition Melting point range (°C) 100% A 125-126 75% A-25% B 115-120 65% A- 35% B 128-131 50% A- 50% B 135-140 100% B 151-152 Can you suggest what additional points you need to give a more accurate measure of the eutectic point?
You are given a sample of polypropylene and wish to find out the volume % crystallinity. You know that the density of 100% crystalline polypropylene (ρc) is 0.946 g/cm3, and the density of 100% amorphous polypropylene (ρa) is 0.855 g/cm3. Through your careful measurements, you determine the density of the sample (ρs) is 0.93 g/cm3. Use the following equation to determine the volume % crystallinity (ν) of your sample. Enter your answer with 1 decimal place. Answer is 82.4 Another sample of polypropylene has a 68 volume percent crystallinity. What is the density of the sample? Enter your answer is g/cm3. ( I need help with this second question. The answer is .917, i just can't get to that.) Hint: use the values and equation from the previous problem.
You are given a sample of polypropylene and wish to find out the volume % crystallinity. You know that the density of 100% crystalline polypropylene (ρc) is 0.946 g/cm3, and the density of 100% amorphous polypropylene (ρa) is 0.855 g/cm3. Through your careful measurements, you determine the density of the sample (ρs) is 0.93 g/cm3. Use the following equation to determine the volume % crystallinity (ν) of your sample. Enter your answer with 1 decimal place. Another sample of polypropylene has a 68 volume percent crystallinity. What is the density of the sample? Enter your answer is g/cm3. I can answer the first part of the question. I just don't know how to do the second question?
What is the average molar mass of a gas containing the following by mass % composition: CO2 = 10 O2 = 3 CO = 3 H2O = 6 and N2 Please show your complete solution and write clearly. Thank you.
Metal A (Tm=860 oC) and metal B (Tm=620 oC) were fully dissolved in each other in the liquid state. The ultimate solubility of B in A is 12% at 460 oC which decreasing with decreasing temperature to 3% at room temperature while the maximum solubility of A in B is 7% at 460 oC still constant to room temperature. A and B form eutectic at 460 oC and 48 % of B. construct phase diagram for A-B alloying system, label all phases and temperatures, and answer the following: a) 28 wt % A alloy is slowly cooled from 720 oC at what temperature does the first solid phase is formed? What is the composition of this solid phase? For this alloy what is the mass fraction of the phases at, 600 oC, 300 oC ,and TR? c) What is the ?composition of the phases in (b)