A diffusion couple of two metals, A and B, was fashioned as shown:Diffusion of A atomsA-B alloyBDiffusion of B atomsAfter a 690 hour heat treatment at 1120°C the concentration of A is 1.8 wt% at the 3.2 mm position within Metal B. At whattemperature (in Kelvin) must the diffusion couple need to be heated to produce this same concentration at a 2.3 mm positionafter 690 h? The preexponential and activation energy values for the diffusion of A in B are 1.9 x 104 m²/s and 239 kJ/mol,respectively.

Answered: Image /qna-images/answer/bf6935a7-1157-46cc-87bd-67f20bf63e9b.jpg

A diffusion couple of two metals, A and B, was fashioned as shown: Diffusion of A atoms K A-B alloy B Diffusion of B atoms After a 690 hour heat treatment at 1120°C the concentration of A is 1.8 wt% at the 3.2 mm position within Metal B. At wha temperature (in Kelvin) must the diffusion couple need to be heated to produce this same concentration at a 2.3 mm positio after 690 h? The preexponential and activation energy values for the diffusion of A in B are 1.9 x 104 m²/s and 239 kJ/mol, respectively.

A diffusion couple of two metals, A and B, was fashioned as shown: Diffusion of A atoms K A-B alloy B Diffusion of B atoms After a 690 hour heat treatment at 1120°C the concentration of A is 1.8 wt% at the 3.2 mm position within Metal B. At wha temperature (in Kelvin) must the diffusion couple need to be heated to produce this same concentration at a 2.3 mm positio after 690 h? The preexponential and activation energy values for the diffusion of A in B are 1.9 x 104 m²/s and 239 kJ/mol, respectively.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

büt4. The following figure shows a plot of the logarithm (to the base 10) of the diffusion coefficient versus reciprocal of the absolute temperature, for the 4 - diffusion of iron in chromium. Determine values for the activation energy and preexponential. R = the gas constant, 8.31 J/mol.K or 8.62 x 10-5 eV/atom.K 10-15 10-16 0.55 0.60 0.65 0.70 Reciprocal temperature (1000/K) Diffusion coefficient (m2/s)
(c) Consider an alloy that is undergoing carburizing process, initially has a uniform carbon concentration of 0.27 wt% and is to be treated at 950oC (1750oF). If the concentration of carbon at the surface is suddenly brought to and maintained at 1.32 wt%, how long will it take to achieve a carbon content of 0.85% at a position 0.7 mm below the surface? The diffusion coefficient for carbon in iron at this temperature is 1.6 x 10-11 m2/s; assume that the steel piece is semi-finite.
The figure below shows five different steady-state concentration profiles from five separate tests, which had the same gas across identical membranes at the same temperature. Rank the diffusion flux of the five concentration profiles from lowest to highest. Using bullet points explain your answer. C(x)' (a) (b) (c) (d) (e) Membrane Thickness
Problem 1. A sheet of BCC iron 1 mm thick was exposed to a carburizing gas atmosphere on one side and a decarburizing atmosphere on the other side at 725°C. After having reached steady state, the iron was quickly cooled to room temperature. The carbon concentrations at the two surfaces of the sheet were determined to be 0.012 and 0.0075 wt%, respectively. Compute the diffusion coefficient if the diffusion flux is 1.4 × 10 -³ kg/m²-s.
The diffusion coefficients for species A in metal B are given at two temperatures: D (m²/s) 7.81 x 10-17 7.70x 10-16 i (b) Determine the value of Do. (a) Determine the value of the activation energy Qd (in J/mol). i T (°C) 1030 i 1260 J/mol m²/s (Use scientific notation.) (c) What is the magnitude of D at 1180°C? m²/s (Use scientific notation.)
Using the Tabulation of Diffusion Data, answer the following: (a) Calculate the diffusion coefficient for Cu in Al at 520'C. 7.18e-14 m2/s (Use scientific notation.) (b) What time (in h) will be required at 620°C to produce the same diffusion result (in terms of concentration at a specific point) as for 12hat 520 C? i 2.52
3. A BCC iron alloy containing 0.05 wt% C is carburized at 1050°C such that the carbon concentration is 0.5 wt% at a distance 2mm from the surface. Meanwhile, the carbon concentration at the surface is kept constant at 1.5 wt% C. a. What is the value of the diffusion constant for carbon diffusing into BCC Fe at 1050 °C? Show all work. Write the relevant equation for the diffusivity within this box: Write the values of all of the parameters in the equation above within the box below: Write your final answer for the diffusivity within this box: b. Determine the diffusion time required to achieve the carbon profile described above. Show all work. Write the relevant equation needed to solve this problem within this box: Write the values of all of the given parameters in the equation above within the box below: Write the value for erf(z) within this box:
Mechanical Engineering At approximately what temperature (in Kelvin) would a specimen of an alloy have to be carburized for 1.3 h to produce the same diffusion result as at 760°C for 14 h? Assume that values for Do and Qdare 3.6 x 10-6 m²/s and 163 kJ/mol, respectively.
A diffusion couple of two metals, A and B, was fashioned as shown in Figure 5.1. After a 26 hour heat treatment at 1170°C (and subsequent cooling to room temperature) the concentration of A is 4.0 wt% at the 11-mm position within metal B. If another heat treatment is conducted on an identical diffusion couple, only at 701°C for 26 hours, at what position (in mm) will the composition be 4.0 wt% A? The preexponential and activation energy values for the diffusion of A in B are 2.4 x 10-4 m²/s and 154 kJ/mol, respectively. i mm
What temperature is required to obtain 0.4%C at a distance of 0.3 mm beneath the surface of a 0.22% C steel in 2h, when 1.1% C is present at the surface? Assume that the iron is FCC. (Please see figure 5.12 below for diffusion coefficient data. Please use your notes for a table of erf() function values table of erf() fun Diffusion coefficient D (cm²/s) 10-3 !! ! ! ! ! 10- 10-5 10-9 10-10 10-11 10-12 10-13 10-14 Temperature (°C) 2000 1500 1200 1000 900 800 700 600 wwwwwwwwwwwwwww in graphite Mg in MgO Ca in CaO H in FCC iron Cin FCC iron Fe in FCC iron Fe in BCC iron H in BCC iron 104 T(K) C in BCC iron Fe in FeO 500 10-15 4 5 6 7 8 9 10 11 12 13 Figure 5-12 The diffusion coefficient D as a function of reciprocal temperature for some metals and ceramics. In this Arrhenius plot, D represents the rate of the diffusion process. A steep slope denotes a high activation energy.
What temperature is required to obtain 0.4%C at a distance of 0.3 mm beneath the surface of a 0.22% C steel in 2h, when 1.1% C is present at the surface? Assume that the iron is FCC. (Please see figure 5.12 below for diffusion coefficient data. Please use your notes for a table of erf() function values Diffusion coefficient D (cm²/s) ܐ ܐ ܐ ܐ 10- 10-5 10- 10-10 10-11 10-12 10-13 10-14 10-15 Temperature (°C) 2000 1500 1200 1000 900 800 700 600 Cin graphite Mg in MgO Ca in Cao Hin FCC iron C in FCC iron Fe in FCC iron Fe in BCC iron H in BCC iron C in BCC iron Fe in FeO 500 5 6 7 8 9 10 11 12 13 104 T(K) Figure 5-12 The diffusion coefficient D as a function of reciprocal temperature for some metals and ceramics. In this Arrhenius plot, D represents the rate of the diffusion process. A steep slope denotes a high activation energy.
Compare the diffusion coefficients (in cm²/s) of nitrogen in BCC and FCC iron at the allotropic transformation temperature of 912°C. Decc -153606 X Your response differs from the correct answer by more than 10%. Double check your calculations, cm²/s -1976-7 Dicc x Your response differs significantly from the correct answer. Rework your solution from the beginning and check each step carefully. cm2/s